Wave soldering process defectives and handling solution

High melting temperature of lead-free solder requires higher operating temperatures, which increases the risk of soldering quality defects, the following problem will happened:  Solder peeling ,solder smearing,solder bridging, solder balls, dissolved copper pad.

Normally we will take the following handling solution:

1. Solder peeling

PCB solder peeling is due to the thermal expansion difference between the PCB base material Resen /glass FR-4 material and the copper hole or copper lead.

After the PCB leaving the solder, the connecting parts temperature cool to room temperature. At this stage, the curing heat diffusion to solder area, prompting the joints as well as all the parts near the temperature increases.

When all of the curing energy fully released, solder temperature gradually to room temperature. Then solder begins to solidify, the circuit board was cooled, and to restore its original planar shape.

This movement has brought to the surface of the solder joint considerable pressure, but at this stage is still strong joints. Therefore, this pressure may cause the pads float away.

2.SolderTrailing

Wired refers only outside the region of the Nozzle solder residue, its contour edge related with the nozzle.

These residues are generally due to solder melting caused the collapse.

These wired contain solder particles of different shapes, different sizes, such as network and tin oxide thin solder balls, but most of these particles are very small.

Use the right amount of flux to the nozzle area can be cleared completely covered tailing multimodal nozzle next.

Under no circumstances flux, solder resist on the solder can also cause tailing.

Experiments show that only the amount of solder temperature and flux of these two parameters have a significant impact on the smearing.

So when there is tailing case, you should try to adjust the amount of flux. In addition, the outer edge of the nozzle apply more solder flux helps reduce temperature.

Use SnPB, solder temperature can be reduced to 260 ?. After lowering the temperature enough to complete the through-hole filling.

3.Solder bridges

If the solder began to flow along the pin, as shown, PIN place left foot will slip away from the solder nozzle.

At this time, the solder cools, solidification, forming bridging. Horizontal welding can reduce the risk of instability in the solder flow.

Unstable solder flow. Lead-free solder nozzle deviates along pin flow trends

In a dual in-line package process, if properly designed to avoid bridging.

Pin shorter, smaller pad spacing between PIN feet wide can reduce the risk of some form of bridging.

Taguchi experiment shows the influence of machine parameters. 10 mg / cm2 or more, the amount of flux and solder temperature low to prevent the formation of bridging the best combination.

4.Solder balls

Solder ball is mainly due to high temperatures and become more viscous solder resist produced. In addition, more flux than other substances produced solder balls. In a dual in-line package soldering process, solder balls usually appear between individual PIN foot

5.Copper pad dissolved

Higher soldering temperatures, the risk of dissolution of copper into the solder. Because lead-free solder containing more tin, at high temperatures, the dissolution rate of copper circuit board has accelerated dramatically.

On the selective soldering peak flow of solder joints formed contact more frequently (robot speed 1mm / sec or slower), the higher soldering temperature (> 300 oC), the greater the risk.

In addition to setting the appropriate parameters for the machine, thick copper layer is also very important, because of this, solder copper content should be checked once every two months to ensure that no more than 1% copper content; otherwise, the reliability of large joints discount.

Select the appropriate parameter, selective soldering can be successfully used. If necessary, it can be coated as a problem more elements each infiltration flux, soaked longer without other elements around because the temperature is too high and damage.

Flason Electronic Co.,ltd provide a full SMT assembly line solutions, including SMT Reflow Oven,  Wave Soldering Machine,  Pick and Place Machine,  SMT Stencil Printer,  SMT AOI SPI Machine,  SMT Reflow Oven,  SMT Peripheral Equipment,  SMT Assembly line,  SMT Spare Parts  etc any kind SMT machines you may need, please contact us for more information: wechat whatsapp:+8613691605420, Skype: flasonsmt, Email: sales@flason-smt.com
FAQ
1) This is the first time I use this kind of machine, is it easy to operate?
There is English manual or guide video that show you how to use machine.
If you still have any question, please contact us by e-mail / skype/ phone /trademanager online service.
2) If machine have any problem after I receive it, how can I do ?
Free parts send to you in machine warranty period.
If the part is less than 0.5KG, we pay the postage.
If it exceeds 0.5KG, you need to pay the postage.
3) MOQ ?
1 set machine, mixed order is also welcomed.
4) How can I buy this machine from you? ( Very easy and flexible !)
A. Consult us about this product on line or by e-mail.
B. Negotiate and confirm the final price , shipping , payment methods and other terms.
C. Send you the proforma invoice and confirm your order.
D. Make the payment according to the method put on proforma invoice.
E. We prepare for your order in terms of the proforma invoice after confirming your full payment.
And 100% quality check before shipping.
F.Send your order by air or by sea.
5)Why choose us ?
A. Gold supplier on Alibaba !
B. Trade assurance to US$54,000 !
C. Best price & Best shipping & Best service !